Different welding wires yield different anodizing results. CFC recommends that 5356 wire be used for 6061 aluminum to avoid darkening of the weld under anoditic coating.DO NOT USE 4043 WIRE. We also recommend NOT to mix different aluminum specifications (e.g. 6061 and 6063) as the anoditic finish will be visibly different for the two metals. (see examples below).
Notice the visual difference between 6061 and 6063 spec. below
(Keep this in mind if you consider mixing different alloys in one part)
NOT FOLLOWING RAILING DRAINAGE GUIDELINES WILL RESULT IN PART DAMAGE
To better ensure the highest quality anodizing and coloring results for railings, we have compiled the following checklist of guidelines and techniques which we suggest you apply
• Always use the appropriate alloy for anodizing. Extrusions should conform to AA 6063 T5 or T6 specifications. Aluminum sheet should conform to AA 5005 specifications.
• Never include non-aluminum materials in rails and rail assemblies.
• Use AA 5356 alloy filler rod to fabricate welded handrails, avoiding AA 4043 (which will turn a grey color in the clear anodizing process and could burn in the 2-step process).
• Avoid excessive heat in welding, as this may cause a temper change in the weld area which could affect coloring, causing a ‘halo’ around the weld.
• Use care in handling aluminum during and after fabrication, making sure all who come in contact with the metal wear gloves. Although the etching process may remove some light surface damage, anodizing will not cover or remove most visible scratches or other damage caused by skin contact—e.g. from perspiration and body oils.
• Avoid sanding or buffing finished surfaces by hand, as anodizing may accentuate surface irregularities that could result from applying less than uniform pressure.
• Rail sections should be no larger than 31.5 feet in length, 6 feet in height, and 26 inches in width to fit in CFC’s tanks. Please call for advice if product approaches or exceeds any of these dimensions.
• Drill holes (3/8-inch minimum diameter) at strategic points to allow for proper submersion in tanks and drainage upon removal. Holes should typically be drilled at each horizontal and vertical connection, with holes at the top for air admission and at the bottom for drainage, as necessary. (see Figure 1 for examples)
• Flat surfaces sandwiched together may also present difficulties for entrapment and subsequent seepage of anodizing chemicals.
Visit our news section for an important update on our Hardcoating line!
CAROLINA FINISHING AND COATING, LLC
441 Countryside Rd
Kings Mountain, NC 28086
Phone: +1 704/7308233 +1 704/7308233
Mr. Maurice Badawy brings 24 years of experience and knowledge in the aluminum anodizing business to CFC, and has assembled a highly qualified staff with over 95 years of experience combined. Together we are CFC Anodizing, bringing you unsurpassed quality and customer service.